ISO 1043 abbreviationISO 1043PA6-GF60ISO 16396 designationISO 16396PA6,GF60,M1,S14-220

DensityISO 11831.69 g/cm3Humidity absorptionISO 62 | T=23°C / 50%RH1 %Water absorptionISO 62 | T=23°C / sat.3 %Molding shrinkage, parallelISO 294-4, 2577 | 72 hrs, 23°C, 50% RH0.1 – 0.3 %Molding shrinkage, normalISO 294-4, 2577 | 72 hrs, 23°C, 50% RH0.2 – 0.4 %Viscosity numberISO 307 | 96% H2SO4125 cm3/g

Tensile modulusISO 527-1/-2 | 1 mm/min22000 / 14500 MPaStress at breakISO 527-1/-2 | 5 mm/min250 / 160 MPaStrain at breakISO 527-1/-2 | 5 mm/min2.5 / 3.5 %Flexural modulusISO 178 | 2 mm/min20000 / 13500 MPaFlexural strengthISO 178 | 2 mm/min390 / 260 MPaCharpy impact strength, +23°CISO 179/1eU | +23°C85 / 90 kJ/m2Charpy impact strength, -30°CISO 179/1eU | -30°C80 / 80 kJ/m2Charpy notched impact strength, +23°CISO 179/1eA | +23°C17 / 22 kJ/m2Charpy notched impact strength, -30°CISO 179/1eA | -30°C12 / 12 kJ/m2Izod impact strength, +23°CISO 180/1U | +23°C80 / 90 kJ/m2Izod notched impact strength, +23°CISO 180/1A | +23°C17 / 21 kJ/m2

Melting temperature, 10°C/minISO 11357-1221 °CTemp. of deflection under load, 0.45 MPaISO 75 | 0.45 MPa220 °CTemp. of deflection under load, 1.80 MPaISO 75 | 1.80 MPa212 °CVicat softening temperatureISO 306 | 50°C/h – 50N210 °C

Volume resistivityIEC 62631-3-11E+016 ohm.mSurface resistivityIEC 62631-3-11E+014 ohmComparative tracking indexIEC 60112 | Solution A500 V

Flammability, 1.5 mmUL 94 | 1.5 mmHBGlow-wire flammability index, GWFIIEC 60695-2-12 | 1-3 mm650 °CBurning rate, FMVSS, Thickness 1 mmFMVSS 302< 100 mm/min

Drying temperature/time75-85°C / 2-4h (with dew point of dried air < -30 °C)Recommended melt temperature260 – 290Recommended mould temperature90 – 100